Chemical composition

High quality carbon round steel rods and hot rolled (or continuous casting) round steel rods are used as material of hot rolled grinding media baIIs. The diameter of round steel rods should be equal to the nominal diameter of grinding baIIs. Normally, the length of each round steel rod is 6M.
Chemical Composition of grinding balls in our company is as follows::

C:0.42-0.90% Si:≤2.0%
Cr:≤1.0% Mo,V,Ti,Cu:≤0.5%
Ni:≤0.5% P:≤0.050%
Mn:≤1.2% S:≤0.050%

 

B2 material

C:0.75-0.85% Si:0.15-0.35%
Cr:0.50-0.60% Mo,V,Ti,Cu:≤0.5%
Ni:≤0.5% P:≤0.050%
Mn:0.70-0.90% S:≤0.050%

 

B3 material

C:0.58-0.66% Si:1.40-1.90%
Cr:0.70-0.90% Mo,V,Ti,Cu:≤0.5%
Ni:≤0.5% P:≤0.050%
Mn:0.65-0.80% S:≤0.050%

 

B6 material

C:0.70-0.90% Si:0.20-0.40%
Cr:0.80-1.0% Mo,V,Ti,Cu:≤0.5%
Ni:≤0.5% P:≤0.050%
Mn:0.85-1.05% S:≤0.050%
 

We could adjust the above chemical composition according to users' specific requirements,and balls of specific types of steel appointed by users could be produced as well.

Microstructure

martensite+carbride

1


Mechanical properties

Microstructure

Impact Toughness(J/cm2)
(Different according to ball size)
Average Volumetric Hardness(HRC) Dropping times without breakage
M+C ≥8 60-65 ≥5000
M-Martensite C-Carbide

 


Product shape.dimension,the oretical weight and hardness

 

Hot rolling grinding ball

(mm)
Round steel bar dia
(mm)
Steel ball dia
(kg/per piece)
Weight
(HRC)
Surface hardness
(HRC)
Core hardness
15 16±1 0.015 62-65 62-65
20 20.8±1 0.037
25 28.0±1 0.072
30 31.2±1 0.125
35 36.2±1 0.198 62-65 61-64
10 41.6±1 0.296
45 46.8±1 0.421
50 52.0±1 0.578
55 57.2±1 0.769
60 62.4±1 0.999
65 67.6±1 1.270 60-63 59-62
70 72.8±1 1.586
75 78.0±1 1.951
80 83.2±1 2.367
85 87±1 2.5243 59-64 57-62
901 92±1 2.9964
95 97.5±1 3.5241
100 103±2 4.1103
105 108±2 4.7582 58-63 55-62
110 112.6±2 5.4710
115 117.4±2 6.2512
120 123±2 7.1026
125 128±2 8.0279

 

Hot forged grinding ball

Round steel bar dia(mm) Steel ball dia(mm) Surface hardness(HRC) Core hardness(HRC)
80±1 2.1045 59-64 57-62
85±1 2.5243
90±1 2.9964
95±1 3.5241
100±2 4.1103
105±2 4.7582 58-63 55-62
110±2 5.4710
115±2 6.2512
120±2 7.1026
125±2 8.0279
130±2 9.0303 58-63 55-62
135±2 10.1076
140±2 11.2728
145±2 12.5243
150±2 13.8651 57-62 55-61
153±2 14.8123

 